ABSTRACT
The aims of this study were: To evaluate the surface hardness of simulated dentin caries lesions treated with either silver nanoclusters (AgNCls) synthesized in polymethacrylic acid (PMAA) or 38% silver diammine fluoride (SDF), as well as observe the penetration of the treatment solutions into the simulated caries lesions. Dentin blocks 4 mm thick obtained from caries-free third molars were sectioned and then simulated caries lesions on the occlusal dentin surfaces were created. Each specimen (n = 8) was divided into four sections: (A) treated with 20% AgNCls/PMAA; (B) treated with SDF 38% (FAgamin, Tedequim, Cordoba, Argentina); (C) sound tooth protected by nail-varnish during artificial caries generation (positive control); and (D) artificial caries lesion without surface treatment (negative control). AgNCls/PMAA or SDF were applied on the simulated lesions with a microbrush for 10 s, then excess removed. The surface hardness was measured by means of Vickers indentation test. To trace the depth of penetration, up to 400 µm, of silver ions, elemental composition of the samples was observed using EDX, coupled with SEM, and measured every 50 µm from the surface towards the pulp chamber. Laser Induced Breakdown Spectroscopy (LIBS) was also employed to trace silver ion penetration; the atomic silver line 328.06 nm was used with a 60 µm laser spot size to a depth of 240 µm. Student's-t test identified significant differences between treatment groups for each depth and the Bonferroni test was used for statistical analysis of all groups (p < 0.05). Mean surface hardness values obtained were 111.2 MPa, 72.3 MPa, 103.3 MPa and 50.5 MPa for groups A, B, C and D respectively. There was a significant difference between groups A and C compared with groups B and D, the group treated with AgNCls/PMAA achieved the highest surface hardness, similar or higher than the sound dentin control. A constant presence of silver was observed throughout the depth of the sample for group A, while group B showed a peak concentration of silver at the surface with a significant drop beyond 50 µm. The 20% AgNCls/PMAA solution applied to simulated dentin caries lesions achieved the recovery of surface hardness equivalent to sound dentin with the penetration of silver ions throughout the depth of the lesion.